EBSD study of strain dependent microstructure evolution during hot deformation of a typical nickel-based superalloy

摘要

The microstructure evolution of a typical nickel-based superalloy was studied in the strain range of 0.1-0.9 at 1110 degrees C/0.01 s(-1) by using the electron backscattered diffraction technique. It was found that the evolution of recrystallized microstructures, grain boundary characteristics, and textures was closely related to strain level. With the increasing strain level, the fraction of equiaxed dynamic recrystallization (DRX) grains increased significantly at the expense of the large non-recrystallized grains, and there was a decrease in total low angle grain boundaries fraction and a simultaneous increase in the fraction of high angle grain boundaries. In addition, the occurrence of DRX promoted the formation of Sigma 3 boundaries, and the coherent Sigma 3 boundaries were much easier to form at the strain above 0.5. On the other hand, 100 component of the textures became stronger with the increasing strains, and the lack of 111 orientations can also be observed in the textures at high strains above 0.7.