Superplastic Deformation Behavior in Mg-Al Alloy, AZ91, Grain Refined by Isothermal-rolling

摘要

The isothermal rolling mill, which allows a large preform for materials having poor workability, has been developed. AZ91 alloy sheets made from Mg-9Al-1 Zn tempered to a fine grain size by recrystallization have been prepared and tensioned at elevated temperatures. The maximum total elongation reached 170% and the m-value was found to be 0.5 in range of 1.0x10~(-4)s~(-1) to 2.5x10~(-4)s~(-1) except at the testing temperature of 573 K. The activation energy required for high temperature deformation has been calculated to be about 124 kJ·mol~(-1), which is almost equal to the self-diffusion energy of Mg for volume diffusion. Therefore, the superplastic deformation of the recrystallized AZ91 has been accompanied by a volume diffusion.