Comparative study of the fire protection performance and thermal stability of intumescent fire-retardant coatings filled with three types of clay nano-fillers

摘要

The fire protection and thermal stability properties of intumescent fire-retardant coatings filled with three various clay nano-fillers (layer double hydroxide [LDH], montmorillonite [MMT], and sepiolite) were compared by fire protection tests and thermo-gravimetric analysis. The fire protection tests show that the incorporation of three fillers improves the fire protection properties of the intumescent fire-retardant coatings and the addition of 1 wt% sepiolite exhibits the lowest flame spread rating of 9.9 and equilibrium backside temperature of 164.5 degrees C at 900 seconds. TG analysis shows that the incorporation of nano-fillers imparts a considerable enhancement of thermal stability and char formation to the intumescent coatings. Especially, the coating with 1 wt% sepiolite acquires the highest residual weight of 34.2% among the samples. Char residue analysis presents that the introduction of clay nano-fillers plays a positive role in enhancing the compactness and anti-oxidation ability of the char residues, and this positive effect as well as the flame-retardant efficiency depends on the types of clay nano-fillers. The three types of layered clay nano-fillers exhibit synergistic flame-retardant effectiveness in the order of sepiolite > MMT > LDH.