Effect of Hexamethyldisiloxane (HMDSO)/Nitrogen Plasma Polymerisation on the Anti Felting and Dyeability of Wool Fabric

摘要

This work is focused on the characterisation of the physical and surface properties of plasma coated wool fabric. A thin film was deposited on wool fabric samples by means of the plasma polymerisation of hexamethyldisiloxane (HMDSO) and differences between such plasma-treated and untreated fabrics were evaluated. The films deposited were characterised by means of Fourier transform infrared (FTIR) spectroscopy. Also the surface morphology of samples was studied using a scanning electron microscope (SEM). Hydrophobic properties of the samples were tested using the water drop test. The results show that by plasma polymerisation, hydrophobic properties of the wool surface change to super hydrophobic. The main aim of the HMDSO/N2 plasma polymerisation of wool fabrics is to improve anti felting properties and dyeing behaviour.%W artykule przedstawiono wyniki badań możliwości modyfikacji właściwości technologicznych tkaniny wełnianej, w tym hydrofobowości, zabarwialności barwnikiem kwasowym, odporności na spilśnianie oraz kurczliwości w kąpielach wodnych, w wyniku wytwarzania na powierzchni włókien cienkiej warstewki spolimeryzowanego HMDSO (heksametyldi-siloksanu). Warstewka ta wytwarzana jest poprzez polimeryzacją HMDSO w środowisku niskociśnieniowej plazmy niskotemperaturowej (LTP). Badania przeprowadzony przy zastosowaniu spektroskopii FTIR oraz mikroskopii SEM. Niezależnie od tego badano hy-drofobowość powierzchni testem kroplowym. Wyniki wykazały, że powierzchnia wykazała charakter super-hydrofobowy.