GFRPを使用する下水道更生管の耐久性迅速評価法

摘要

There are many old sewer pipes which may cause accidents in Japan. Rehabilitated pipes called CIPP (Cured In Place Pipe) use GFRP can repair and renewal those without digging. The lifetime prediction is standardized by ISO, JIS, etc. The rehabilitated pipes are tested to calculate design values of the value for 50 years by the long-term examination of 10,000 hours. It is indicated by "guidance of pipe rehabilitation (proposal)" which writes the time problem of a long-term examination clearly as a future subject. Then, it was a deed about the stress relaxation test, the time-temperature superposition principle which is generally used by GFRP and established was applied to life prediction for rehabilitated pipes, and it was compared with the long-term examination. Consequently, the validity of this lifetime prediction method could be verified. And the lifetime prediction method in the short time to the rehabilitated pipes was able to be established.%日本では老朽化した下水道管きょが原因となり陥没事故が発生している．これに対し下水道管きょを非開削で修復・更新できる管きょ更生工法が開発されている．GFRP製の下水道更生管はISOやJISなどで耐久性評価法が規格化されている．「管きょ更生工法における設計・施工管理の手引き（案）」は寿命として定められた50年後の特性値を求めるために10,000時間（約1年2ケ月）の長期クリープ試験を規定している．これは材料開発の遅れを助長しており，耐久性の迅速評価法が求められている．これに対し1週間の応力緩和試験と高分子の耐久性迅速評価法として一般的な時間-温度換算則を組み合わせてマスターカーブを得る手法を提案する．この手法はGFRP製下水道更生管にも適用可能であるが，複数種類の更生管で確認した事例はない．本論文は日本管路更生工法品質確保協会に所属する7協会8工法の下水道更生管を使用し，長期クリープ試験の代替法としてこの手法による耐久性評価を提案する．