Wear tests were performed using a ball-on-disc tribological tester. In this study, 42CrMo4 steel disc of hardness 40 HRC co-acted with 100Cr6 steel ball with hardness of 60 HRC. Disc surfaces were created using vapor blasting to obtain values of the Sq parameter close to 5 μm. However, other disc surface topography parameters varied. Dry friction tests were carried out. Wear levels of discs and balls were measured using a white light interferometer Talysurf CCI Lite. It was found that the surface topography had a significant impact on tribological properties under dry sliding conditions. The research also allowed to identify significant dependencies between surface topography parameters and wear.
展开▼
机译:使用球盘摩擦摩擦测试仪进行磨损测试。在本研究中,42crmo4硬度40 HRC共用100Cr6钢球,硬度为60 hrc。使用蒸气爆破产生盘表面,以获得接近5μm的SQ参数的值。但是,其他盘表面形貌参数变化。进行干摩擦试验。使用白光干涉仪Talysurf CCI Lite测量磨损水平和球。发现表面形貌对干燥滑动条件下的摩擦学性质产生重大影响。该研究还允许识别表面形貌参数和磨损之间的显着依赖性。