Ultrasonically assisted synthesis of lead oxide nanoflowers using ball milling

摘要

The experimental results on the ultrasonically assisted synthesis of lead oxide nanoflowers using ball milling have been reported in the present work. Lead oxide nanoflowers were prepared employing mixed ligands by subjecting the formed precipitate to ultrasonication and grinding/ball milling. The effect of ball milling as well as fine grinding in agate mortar on the microstructure and surface morphology of the lead oxide was studied. The characteristics of synthesized PbO were studied using X-ray diffraction, X-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy and field emission scanning electron microscopy techniques. XRD results demonstrated the tetragonal phase of PbO with crystallite size of around 25?nm and strain of 3.6?×?10?3 calculated from Williamson–Hall plot. FESEM images manifested the formation of nanodiscs and nanoflowers with a diameter of around 300?nm and thickness of 50?nm. XPS spectra revealed the formation of PbO with photoelectron peak of Pb 4f and O 1?s lied at 137.68 and 529.96?eV. Moreover, FTIR spectrum exhibited Pb–O bond peak in the range of 400–530?cm?1.