Relation between Chemical Composition and Physical Properties of C-S-H Generated from Cementitious Materials

摘要

Calcium silicate hydrate (C-S-H) is a dominant hydration product of cementitious materials. Therefore, its chemical composition and physical properties affect the performance of concrete. The purpose of this study is to investigate the chemical composition (CaO/SiO_(2) molar ratio (Ca/Si ratio), and H_(2)O/SiO_(2) molar ratio (H_(2)O/Si ratio)) and physical prop-erties, such as density and specific surface area, of C-S-H. These factors are measured using synthesized C-S-H samples and C-S-H generated from various cementitious materials. Experimental results show that the H_(2)O/Si ratio of C-S-H is proportional to the Ca/Si ratio independent of the mix proportion, curing temperature and type of binder. The density and specific surface area of C-S-H are affected by its Ca/Si ratio. A linear relationship is observed between the Ca/Si ratio and density of C-S-H independent of the mix proportion, curing temperature and type of binder. An inversely proportional relationship is found between the Ca/Si ratio and specific surface area of C-S-H.