ポーラスコンクリートの凍害劣化に及ぼすスケーリング抵抗性の影響

摘要

Frost resistance of porous concrete (PoC) was examined based on the scaling and water absorption property under freeze-thaw action with JIS A 1148 procedure A/B and RILEM CIF/CDF tests. As a result, water absorption behavior of PoC could be subdivided into two parts: water absorption under isothermal temperature and frost suction during freezing and thawing cycles. Little amount of frost suction made PoC more resistant to frost scaling. Air entraining was effective against frost scaling of PoC, as well as that of conventional concrete. In addition, frost damage of PoC which has a service period of 10 years at cold climate corresponded to that of the replicated PoC. This replicated PoC had been subjected to approximately 40 freezing and thawing cycles with CDF test. In this study it was found that if the scaling quantity of PoC exceeds 300g/m2, the relative dynamic modulus of elasticity and the flexural strength sharply decreases. It was confirmed that the scaling resistance was an important factor to evaluate the frost resistance of PoC.%ポーラスコンクリート（以下：PoC）の凍害劣化メカニズムを検討するために，一般的なJIS A 1148 A/B法とともrnにRILEM CIF/CDF法を実施し，スケーリングと凍結融解作用下での吸水挙動がPoCの耐凍害性に与える影響を詳しrnく検討した。PoCの吸水挙動は常温下と凍結融解作用下に分けて考えることができ，凍結融解作用下での吸水量が小rnさいほどスケーリング抵抗性が高いことが明らかとなった。また，普通コンクリートと同様にAE剤の使用がPoCのrnスケーリング抵抗性を向上させることが確認された。さらに，寒冷地で10年間供用されたPoCの劣化程度は，再現rn供試体におけるCDF法の凍結融解40サイクル程度の凍害損傷によく対応していた。本研究の範囲内では，スケーリrnング量が300g/m~2を超えた場合に，相対動弾性係数および曲げ強度比の急激な低下が認められた。PoCのスケーリンrnグ抵抗性は耐凍害性に与える影響が大きく，PoCの耐凍害性評価の指標となり得ることが明らかとなった。