Amorphous TiO2 Nanotubes as a Platformfor Highly Selective Phosphopeptide Enrichment

摘要

This work reports highly selective phosphopeptide enrichment using amorphous TiO2 nanotubes (TiO2NTs) and the same material decorated with superparamagnetic Fe3O4 nanoparticles (TiO2NTs@Fe3O4NPs). TiO2NTs and TiO2NTs@Fe3O4NPs materials were applied for phosphopeptide enrichment both from a simple peptide mixture (tryptic digest of bovine serum albumin and α-casein) and from a complex peptide mixture (tryptic digest of Jurkat T cell lysate). The obtained enrichment efficiency and selectivity for phosphopeptides of TiO2NTs and TiO2NTs@Fe3O4NPs were increased to 28.7 and 25.3%, respectively, as compared to those of the well-established TiO2 microspheres. The enrichment protocol was extended for a second elution step facilitating the identification of additional phosphopeptides. It further turned out that both types of amorphous TiO₂ nanotubes provide qualitatively new physicochemical features that are clearly advantageous for highly selective phosphopeptide enrichment. This has been confirmed experimentally resulting in substantial reduction of non-phosphorylated peptides in the enriched samples. In addition, TiO₂NTs@Fe₃O₄NPs combine high selectivity and ease of handlingdue to the superparamagnetic character of the material. The presentedmaterials and performances are further promising for applicationstoward a whole range of other types of biomolecules to be treatedin a similar fashion.