Ambulatory Evaluation of ECG Signals Obtained Using Washable Textile-Based Electrodes Made with Chemically Modified PEDOT:PSS

摘要

A development of washable PEDOT:PSS (poly(3,4-ethylenedioxythiophene) polystyrene sulfonate) polyamide textile-based electrodes is an interesting alternative to the traditional Ag/AgCl disposable electrodes, usually used in clinical practice, helping to improve medical assessment and treatment before apparition or progress of patients’ cardiovascular symptoms. This study was conducted in order to determine whether physical properties of PEDOT:PSS had a significant impact on the coated electrode’s electrocardiogram (ECG) signal quality, particularly after 50 washing cycles in a domestic laundry machine. Tests performed, included the comparison of two PEDOT:PSS solutions, in term of viscosity with emphasis on wetting tests, including surface tension and contact angle measurements. In addition, polyamide textile fabrics were used as substrate to make thirty electrodes and to characterize the amount of PEDOT:PSS absorbed as a function of time. The results showed that surface tension of PEDOT:PSS had a significant impact on the wetting of polyamide textile fabric and consequently on the absorbed amount. In fact, lower values of surface tension of the solution lead to low values contact angles between PEDOT:PSS and textile fabric (good wettability). Before washing, no significant difference has been observed among signal-to-noise ratios measured (SNR) for coated electrodes by the two PEDOT:PSS solutions. However, after 50 washing cycles, SNR decreased strongly for electrodes coated by the solution that had low viscosity, since it contained less solid contents. That was confirmed by scanning electron microscopy images (SEM) and also by analyzing the color change of electrodes based on the calculation of CIELAB color space coordinates. Moreover, spectral power density of recorded ECG signals has been computed and presented. All cardiac waves were still visible in the ECG signals after 50 washing cycles. Furthermore, an experienced cardiologist considered that all the ECG signals acquired were acceptable. Accordingly, our newly developed polyamide textile-based electrodes seem to be suitable for long-term monitoring. The study also provided new insights into the better choice of PEDOT:PSS formulation as a function of a specific process in order to manufacture cheaper electrodes faster.