Quasi-Living Polymerization of Propene with an Isotactic-Specific Zirconocene Catalyst

摘要

Propene polymerization with isotactic (iso)-specific C2-symmetric rac-Me2Si(2-Me-Benz(e)-Ind)2ZrCl2 (>1) and rac-Me2Si(2-Me-4-Ph-1-Ind)2ZrCl2 (>2) were conducted under various conditions for achieving iso-specific living polymerization of propene. When Complex >1 was activated with trialkylaluminum-free modified methylaluminoxane (dMMAO) at −40 °C, the number-average molecular weight (Mn) linearly increased against the polymerization time to reach Mn = 704,000 within 15 min of polymerization, although the molecular weight distributions was broad (Mw/Mn < 3). Thus, it was found that quasi-living polymerization of propene proceeded in the >1-dMMAO system. The living nature of iso-polypropene was confirmed by the block copolymerization, where the Mn value increased from 221,000 to 382,000 after the addition of 1-octene to yield the block copolymer with a melting point of 150 °C.