Rapid Fabrication of High-Performance CaO-Based Integral Ceramic Mould by Stereolithography and Non-Aqueous Gelcasting

摘要

A high-performance CaO-based integral ceramic mould was fabricated for investment casting by stereolithography (SLA) and non-aqueous gelcasting. The rheology of tert-butyl alcohol (TBA)-based CaO slurries and the effect of gelation parameters on the gelation time and strength of the green body were investigated to obtain a high-quality green body of the CaO-based integral ceramic mould. Then the pre-sintering and sintering processes were optimized to avoid cracks, reduce the sintering shrinkage, and improve the strength of CaO-based ceramic mould. The results showed that the CaO-based slurry with 56 vol % solid loading and 3 wt % dispersant content exhibited high stability and good flowability. The optimized gelation parameters were determined to be a monomer content of 20 wt %, a ratio of crosslinker to monomer of 0.06, an initiator content of 1 wt % and a gelation temperature of 40 °C. A reasonable sintering regime was identified to avoid cracks and guarantee a low shrinkage of 0.6%, a room temperature bending strength of 14.12 MPa and a high temperature (1200 °C) strength of 8.22 MPa. The CaO-based integral ceramic mould fabricated in this study has many advantages including excellent thermal stability, reaction-resistance to molten active alloys, ease of dissolution, and enhanced efficiency and economy in comparison to SiO2 or Al2O3 ceramic moulds.