Sintering behavior of aluminum nitride powder prepared by self-propagating high-temperature synthesis method

摘要

Fully dense aluminum nitride(AIN) ceramics were synthesized by self-propagating high-temperature synthesis(SHS) method using AIN powder as raw material with Y_2 O_3 additive. The sintering behavior was studied at different sintering temperatures and additive contents. The change of phase compositions, secondary phase distributions and grain morphologies during sintering process were investigated. It is shown that fully dense ceramics using AIN powder prepared by SHS method can be obtained when the sintering temperature is above 1830 ℃. Both Y_2 O_3 content and sintering temperature have an important influence on the formation of Y-Al-O phase and grain shape. When Y_2 O_3 content is identified, the grain morphology converts from polyhedron into sphere-like shape with the rise of sintering temperature. At a certain sintering temperature,the grain size decreases with the increase in Y_2 O_3 content. The influencing mechanisms of different YAl-O secondary phases and sintering temperatures on the grain size and morphology were also discussed based on the experimental results.