无外加酸体系中AlSBA¯15为模板,有序介孔炭材料CMK¯3的合成与表征

摘要

在无外加酸体系中改变晶化温度合成AlSBA¯15介孔材料,并以此为刚性模板,蔗糖为碳源,合成出一系列具有不同孔结构的有序介孔炭材料CMK¯3,系统考察晶化温度对AlSBA¯15和其反相复制结构CMK¯3孔道结构的影响。结果显示在无外加酸合成体系中改变晶化温度可对AlSBA¯15的孔道结构进行有效调控,通过结构复制技术可制备出具有不同结构的CMK¯3。控制刚性模板AlSBA¯15的晶化温度为90益,所得介孔炭材料CMK¯3(CMK¯3(90))结构最佳,除介孔排列高度有序外,还具有高比表面积(1688 m2·g-1)和大孔容(0.95 cm3·g-1)。另外,对CMK¯3的微孔性质与刚性模板孔壁中的次级介孔结构的内在联系进行研究,发现调变刚性模板的晶化温度可以有效改善有序介孔炭材料CMK¯3的结构性质。%Highly ordered mesoporous carbons ( OMCs) designated CMK¯3 were synthesized using mesoporous Al¯SBA¯15 with different textural properties as hard templates and sucrose as a carbon source. Al¯SBA¯15 is an ordered mesoporous alumina¯silica synthesized with a soft template, P123. The effect of the aging temperature for the hard templates on the pore structure of CMK¯3 was investigated. X¯ray diffraction, N2 adsorption and transmission electron microscopy were used to characterize the pore structures of the hard templates and the resultant CMK¯3. Result indicates that CMK¯3 with different pore structures can be obtained by tailor¯ ing the pore structures of the hard templates bysimply controlling the aging temperature in an acid¯free medium. The best CMK¯3 possessed a highly¯ordered pore structure, and a very high BET surface area (1 688 m2 ·g-1 ) and pore volume (0. 95 cm3 ·g-1 ) when the hard template was aged at 90 ℃. The microporous character of the CMK¯3 was related to the thickness of the mesopore wall of the hard templates. The textural characteristics of the resultant CMK¯3 can be improved by simply adjusting the aging tem¯ perature in the synthesis of the hard templates to control their mesopore structure.