Direct TEM Observation of Phase Separation and Crystallization in Cu_(45)Zr_(45)Ag_(10)Metallic Glass

摘要

The structural evolution of Cu_(45)Zr_(45)Ag_(10) metallic glass was investigated by in situ transmission electron microscopy heating experiments. The relationship between phase separation and crystallization was elucidated. Nucleation and growth-controlled nanoscale phase separation at early stage were seen to impede nanocrystallization, while a coarser phase separation via aggregation of Ag-rich nanospheres was found to promote the precipitation of Cu-rich nanocrystals.Coupling of composition and dynamics heterogeneities was supposed to play a key role during phase separation preceding crystallization.