Carbon nanotube(CNT)-reinforced AZ91 D alloy composite was fabricated by ultrasonic processing.The microstructure and mechanical properties of the CNTs/AZ91 D composites were investigated.Obvious grain refinement was achieved with the addition of 0.5 wt%CNTs.The SEM observation indicated that CNTs were distributed near the grain boundary or around the inter-grain β-Mg_(17)Al_(12) phase.No evident reaction product was found at the interface between CNTs and AZ91 D matrix.Compared to the monolithic AZ91 D alloy,the yield strength,ultimate tensile strength,and elongation of the 0.5 wt%CNTs/AZ91 D composite were improved significantly.However,the poor interface bonding between CNTs and AZ91 D matrix restricted further improvement in mechanical properties.