Temperature Effects on the Microstructures of Mg-Gd-Y Alloy Processed by Multi-direction Impact Forging

摘要

A high strain rate multi-directional impact forging(MDIF) was applied to a solutionized Mg-Gd-Y-Zr alloy in the temperature range of 350-500℃.Results demonstrate that the dominant deformation mode is twinning at a temperature below 400℃,whereas at a medium temperature of 450℃ considerable continuous dynamic recrystallization was promoted by{10-12} extension twins.At a higher temperature of 500℃,twinning activation was suppressed.New DRX grains were observed but their sizes were much bigger than those resulting from the MDIFed 50 passes at 450℃,which are ascribed to the larger grain boundary mobility and atomic diffusion at 500℃.Moreover,a non-basal weak texture was gained afterward MDIF at each temperature,which is credited to the MDIF process and the minor strain applied in each pass.