Ultra High Molecular Weight Polyethylene(UHMWPE)has been widely used as a bearing material for artificial joint replacementover forty years.It is usually crosslinked by gamma rays irradiation before its implantation into human body.In thisstudy,UHMWPE and UHMWPE/nano-hydroxyapatite(n-HA)composite were prepared by vacuum hot-pressing method.Theprepared materials were irradiated by gamma rays in vacuum and molten heat treated in vacuum just after irradiation.The effectof filling n-HA with gamma irradiation on tribological properties of UHMWPE was investigated by using friction and wearexperimental machine(model MM-200)under deionized water lubrication.Micro-morphology of worn surface was observedbymetallographic microscope.Contact angle and hardness of the materials were also measured.The results show that contactangle and hardness are changed by filling n-HA and gamma irradiation.Friction coefficient and wear rate under deionized waterlubrication are reduced by filling n-HA.While friction coefficient is increased and wear rate is reduced significantly by gammairradiation.The worn surface of unfilled material is mainly characterized as adhesive wear and abrasive wear,and that of n-HAfilled material is mainly characterized as abrasive wear.After gamma irradiation,the degrees of adhesive and abrasive wear forunfilled material and abrasive wear of n-HA filled material are significantly reduced.Unfilled and filled materials after irradiationare mainly shown as slight fatigue wear.The results indicate that UHMWPE and UHMWPE/n-HA irradiated at the doseof 150 kGy can be used as bearing materials in artificial joints for its excellent wear resistance compared to original UHMWPE.
展开▼