Ni-W Catalysts Supported on Mesoporous SBA-15: Trace W Steering CO_(2) Methanation

摘要

A series of Ni-W catalysts supported on mesoporous SBA-15 with different Ni:W ratios(NixW/SBA-15, Ni-5%, x=1, 10, 50) was prepared and fully characterized by powder X-ray diffraction(PXRD), Brunner-Emmet-Teller(BET), transmission electronic microscopy(TEM), H2-temperature programmed reduction(H2-TPR), and X-ray photoelectron spectroscopy(XPS). High-resolution TEM images, XPS measurements, H2-TPR experiments coupled with PXRD results determined the evolution of Ni and W species. It is found that a trace amount of W from H2WO4 can significantly improve Ni dispersion on SBA-15 (Ni50W/SBA-15) with Ni0 and non-stoichiometric WOx species as small as ca. 3.6 nm. The prepared NixW/SBA-15 was utilized for CO_(2) hydrogenation, which showed that a higher W content restrained the CO_(2) hydrogenation while a lower W ratio promoted both conversion rate and selectivity for methane compared with Ni/SBA-15. The Ni50W/SBA-15 catalyst showed the best performance with a 93.3% CO_(2) conversion rate and 99.7% selectivity for methane at 400 oC under 0.1 MPa and maintained ca. 97% initial performance for 24 h. Tracking product evolution experiments by in-situ Fourier transform infrared spectrascopy(FTIR) indicated that a small amount of W can modify the surface of Ni particles by geometric coverage and electronic modification, which facilitates the adsorption of the CO intermedia and results in the formation of CH4. This work provides a new clue to fabricating efficient CO_(2) conversion bimetallic materials.