Orthorhombic LiMnO2 cathode materials were synthesized successfully at lower temperature by sol-gel method. When LiMnO2 precursor prepared by sol-gel method was fired in air, the product was a mixture of spinel structure LiMn2O4and rock-salt structure Li2MnO3, whereas in argon single-phase orthorhombic LiMnO2 could obtain at the range of 750℃ to 920℃. The substitution of Mn by Zn2+ or Co3+ in LiMnO2 led to the structure of LiMnO2 transiting to α-LiFeO2. The results of electrochemical cycles indicated that the discharged capacity of orthorhombic-LiMnO2was smaller at the initial stages, then gradually increased with the increasing of cycle number, finally the capacity stabilized to certain value after about 10th cycles. This phenomenon reveals that there is an activation process for orthorhombic LiMnO2 cathode materials during electrochemical cycles, which is a phase transition process from orthorhombic LiMnO2 to tetragonal spinel Li2Mn2O4. The capacity of orthorhombic LiMnO2 synthesized at lower temperature is larger than that synthesized at high temperature.
展开▼
机译:Lijun WU, Yu ZHANG, Bingjiang LI, Pengxiang WANG, Lishuang FAN, Naiqing ZHANG, Kening SUN Fabrication of layered structure VS_4 anchor in 3D graphene aerogels as a new cathode material for lithium ion batteries
机译:Natural (天然) and units (高单位) nutrients (营养素) 13 one component (成分) Total (综合) Vitality (活力) Samtoh, high natural nutritious foods (食品) of the name is excellent (优秀) a domestic natural raw materials (国产自然原料) using 12 species (利用) and processing (加工处理) and a method of manufacturing (制造方法)