In order to reduce the cost of the austenitic stainless steels(ASSs),the expensive austenite former(nickel) is often substituted by manganese.However,manganese is generally seen to have a detrimental effect on the corrosion resistance.In the present study,the feasibility of laser surface modification of a lean-alloyed ASS(FeCrMn) for enhancing pitting corrosion resistance was investigated.Laser surface modification of FeCrMn was successfully achieved by a 2.3 kW high power diode laser(HPDL).Cyclic polarization tests for FeCrMn after laser surface modification in 3.5% NaCl solution at 25 ℃ were performed by using a potentiostat.The pitting resistance of the laser-modified specimens was found to be significantly improved as reflected by the noble shift in pitting potential.This could be attributed to redistribution of manganese sulphide leading to a more homogenous and refined microstructure.Pitting corrosion resistance of the laser-treated FeCrMn followed by subsequent citric acid passivation was found to be further improved as reflected by the noble shift in pitting potential to 0.18 V.
展开▼