Investigation on Hard Magnetic Properties of Nanocomposite Permanent Magnets with Precipitate-Typed Microstructure by Micromagnetic Finite-Element Methods

摘要

The demagnetization curves were calculated using micromagnetic finite-element method for nanocomposite Pr 2Fe 14B/α-Fe permanent magnets with precipitate-typed microstructure. Due to intergrain exchange coupling, both remanence enhancement and a single magnetic phase behavior in demagnetization curve were found. For the samples with the hard phase as the precipitate and the soft one as the matrix, a coercivity μ 0H c of 0.78 T, a remanence J r of 1.18 T and a large energy product (BH) max of 200 kJ·m -3 are obtained for the sample with hard grain size being 23 nm. While, for the sample with the soft phase as the precipitate, μ 0H c of 0.95 T, J r of 1.24 T and (BH) max of 240 kJ·m -3 are obtained for the sample with soft grain size being 10 nm. The calculating results were compared with the experimental Pr 8Fe 87B 5 ribbons. The dependence of remanence and coercivity on the microstructure was discussed extensively.