For the first time, the undercooling of a magnetostrictive material a near peritectic Tb 0.27 Dy 0.73 Fe 1.90 alloy was realized by vacuum electromagnetic levitation melting and 60 K undercooling was obtained. There is one recalescence behavior during solidification of the undercooled melt,which can attribute to the priority precipitation of REFe 2 phase instead of REFe 3 phase, due to preferential nucleation and higher crystal growth rate of REFe 2 phase and the suppression of peritectic reaction. According to the crystal structural characteristics of REFe 2 and REFe 3, REFe 2 is a Laves phase intermetallics with MgCu 2 type structure, which has similar polytetrahedral structure with short range ordered structure in undercooled melt and has lower potential barrier for nucleation than that of REFe 3,which lead to the preferential nucleation of REFe 2 phase directly from the undercooled melt. Also, the similarity of structures between REFe 2 phase and undercooled melt leads to higher crystal growth rate of REFe 2 phase than that of REFe 3.