常温下以间苯三酚和3-甲醛苯并噻吩作为原料,一步法合成了含硫酚醛树脂.在氩气保护下碳化,成功制备出了硫掺杂多孔碳(S-PC).并利用扫描电镜(SEM)、X射线光电子能谱(XPS)、X射线衍射(XRD)和氮气吸附-脱附仪对材料进行了形貌、结构和性能的表征.实验结果表明,所得样品具有较高比表面积和大量的微孔,经过调控,可以使制备的硫掺杂多孔碳的BET比表面积达到997 m2·g-1,并使其微孔孔体积达到0.44 cm3·g-1.得益于较高的比表面积以及其富含微孔的特性,当材料应用于二氧化碳吸附时,具有较高的CO2吸附量,在273和298 K时分别高达5.13,3.22 mmol·g-1,并具有良好的选择性.%Sulfur doped porous carbon (S-PC) were obtained by direct carbonization of sulfur containing phenolic resins,which were synthesized through one step reaction between phloroglucinol and benzo [b]thiophenc-3-carboxaldehyde under room temperature.The material was characterized by scanning electron microscope (SEM),X-ray photoelectron spectroscopy (XPS),X-ray diffraction (XRD) and N2 sorption-desorption experiments.The obtained porous carbons possess high surface area with abundant of micropores.What's more,ultra-high surface area of 997 m2· g-1 along with ultra-large micropore volume of 0.44 cm3 ·g-1 could be obtained after carefully regulation the concentration of reactants.Owing to these fascinating characters like high surface area and rich of micropores,both high CO2 uptake capacity (5.13 and 3.22 mmol·g-1 for 273 and 298 K respectively) and high selectivity was obtained,which indicating it's promising sorbents for CO2.
展开▼