Preparation and Characterization of Two-component Waterborne Polyurethane Comprised of Water-soluble Acrylic Resin and HDI Biuret

摘要

A two-component waterborne polyurethane(2K-WPU) was prepared by mixing water-soluble acrylic resin and hexamethylene diisocyanate biuret, and then diluted for phase inversion with water. Compared with water-soluble acrylic resin, the phase inversion of 2K-WPU occurs at lower water content. It is indicated by TEM that 2K-WPU parti-cles show a core-shell structure, in which HDI biuret is encapsulated by hydrophilic acrylic resin. 2K-WPU emulsion with HDI biuret has larger particle size and narrower distribution index, while for 2K-WPU emulsion with HDI iso-cyanurate, the latex not only has large particle size, but also has two-peak distribution. FTIR shows that the reaction be-tween HDI biuret and acrylic resin can complete in 12h. In addition, studies on effect of composition of acrylic resin on performance of 2K-WPU show that narrowing the polar difference between water-soluble acrylic resin and HDI biuret and improving the miscibility of two components are the key to prepare the transparent and high gloss films with high crosslinking density.