AlSiCu_(10-10) flame brazing 6063 aluminum alloy was rearched,and microstructure and mechanical properties of brazed joints were tested in the experiments. The interfacial microstructures and brazing phases of brazed joints were analyzed by scanning electron microscopy( SEM) and X-ray energy dispersive spectroscopy( EDS). The strength of brazed joints was aquired by tensile test. The results show that the AlCu_2 and Mg_2 Si phases were formed in the brazing seam,the former is the brittle phase,the Mg_2 Si phases is considered to be the strengthening phase of the aluminum alloy,which can reduce the brittleness caused by AlCu_2. The average tensile strength of brazed butt joint was 115 MPa,and the average shear strength of brazed joint was 26 MPa. Finally,the fracture form and fracture morphology of the brazed joint were analyzed.
展开▼
机译:Microstructural evolution and mechanical properties of FeCoCrNiCu high entropy alloys:a microstructure-based constitutive model and a molecular dynamics simulation study
机译:Etude du Comportement micro-mecanique d'Une Vitroceramique a subst de siO2-al2O3-Li2O en Liaison avec la microstructure(siO2-al2O3-Li2O玻璃陶瓷的微观力学行为及其与微结构的关系研究)