Mg 1- x M x B 2 (M=Li or deficiency) compounds were prepared and their structure and superconducting properties were studied. The results show that nearly single phased Mg 1- x Li x B 2 samples have been obtained while x ≤0.3. With increasing x , lattice parameters a decreases and c shows no obvious change, and the superconducting transition temperature T c of Mg 1- x Li x B 2 decreases. Moreover, loss of superconductivity occurs for sample with x =0.5. For Mg 1- x B 2 nearly single phased samples can be obtained at x =0. MgB 2 coexists with MgB 4 phase and some minor impurity phases while 0< x <0.5. With the increase of x , a and c of MgB 2 decreases and increases, respectively, and T c decreases. The obvious difference in the superconductivity of Mg 1- x Li x B 2 and Mg 1- x B 2 suggests that Li indeed dopes into the structure of MgB 2.
展开▼
机译:平成28年度论文赏受赏轮文:Effect of Si/Fe Composition, Substrate Temperature, and Substrate Orientation on the Structure and Magnetic Properties of Fe-Si Alloy Film
机译:公司治理结构对盈余管理的影响研究—基于民营类上市公司的实证分析 =The Influence of Corporate Governance Structure on Earnings Management at the Listed Non-State-Controlled Firms in China