Compositional graded BaxSr1-xTiO3 (x=0.6, 0.7, 0.8, 0.9, 1.0) (BST) thin films (less than 400 nm) were fabricated on Si and Pt/Ti/SiO2/Si substrates by sol-gel technique. A special heating treatment was employed to form the uniform composition gradients at 700 ℃. The microstructures of the films were studied by means of X-ray diffraction, atomic force microscope and field emission scanning electron microscopy. The results show that the films have uniform and crack-free surface morphology with perovskite structure phase. The small signal dielectric constant (εr) and dielectric loss (tan δ) are found to be 335 and 0.045 at room temperature and 200 kHz. The dielectric properties change significantly with applied dc bias, and the graded thin film show high tunability of 42.3% at an applied field of 250 kV/cm. All the results indicate that the graded BST thin films prepared by sol-gel technique have a promising candidate for microelectronic device.
展开▼
机译:平成28年度论文赏受赏轮文:Effect of Si/Fe Composition, Substrate Temperature, and Substrate Orientation on the Structure and Magnetic Properties of Fe-Si Alloy Film