As-cast and heat-treated 400-18 ductile iron(DI)grade was obtained in different foundry conditions,as metallic charge,Mg-treatment alloy and inoculation.It was found that the Pearlitic Influence Factor(Px)and Anti-nodulizing Complex Factor(K1)have an important influence on property of DI,depending on the Mn and P level,the metallurgical quality of iron melt,rare earth(RE)and inoculation.It was also found that the influence of Mn is depended on the phosphorus and residual elements level in ductile iron.Less than 0.03%P and 0.2%Mn and Px2.0)determines presence of pearlite in as-cast structure,while ferrite structure is obtained after a short annealing heat treatment.Lower level of phosphorus(P1.2.Si has a significant influence on the mechanical properties of heat treated ductile irons:an important decreasing of elongation level and a moderate increasing of yield and tensile strength and their ratio in 150-170 HB typical hardness field.A typical final chemical composition for as-cast 400-18 ductile iron could include 3.5%-3.7%C,2.4%-2.5%Si,max.0.18%Mn,max.0.025%P,max.0.01%S,0.04%-0.05%Mgres.for Px<1.5 and K1<1.1.High purity pig iron,RE-bearing FeSiMg and powerful inoculant are also recommended.
展开▼
机译:Translating Success and Happiness: A Study on Dale Carnegie’s How to Win Friends and Influence People in Chinese Translations =翻译成功,译介幸福:卡内基之How to Win Friends and Influence People译本研究