Microstructure and properties of laser-arc hybrid welding of high-strength low-alloy steel

摘要

Laser-arc hybrid welding has the characteristics of optimal surface formation and greater penetration;it is extensively used in the welding of plates of medium thickness.However, for hybrid welding of lasers, the welding seam cooling rate is rapid;thus, the welding seam has a higher tendency to significantly harden, which has a negative impact on the weld quality of the high-strength low-alloy(HSLA) steel plates of medium thickness.In this study, laser-arc hybrid welding is performed on the BG890 QL HSLA steel produced by Baoshan Iron & Steel Co.,Ltd.,and the quenching tendency of the welded structure is examined.The results demonstrate that the specific growth direction of the columnar crystal structure of the laser-arc hybrid welded joint is obvious.However, at the center and top of the welded seam, there are equiaxed crystals.The impact properties at room temperature and-40 ℃ of the weld area are 58.0 J and 40.0 J,respectively, and those of the heat-affected zone(HAZ) are 147.0 J and 66.5 J,respectively.The impact performance can meet these requirements.Laser-arc hybrid welding of HSLA steel can yield strong and durable welds and the HAZ structure to meet the requirements of engineering applications.