THE MORPHOLOGY AND SIZE CONTROL OF COBALT PARTICLES PRODUCED FROM CONCENTRATED AQUEOUS SOLUTION

摘要

Cobalt basic carbonate particles were precipitated from 1.0mol cobalt nitrate or cobalt sulfate solution with ammonia carbonate. By controlling the zeta-potential of the particles and the ionic strength of the solution, the uniform particles with ellipsoid or rod shapes were obtained. During the precipitation process, the interface tension was diminished to the minimum and therefore the Ostwald ripening and secondary nucleation were both inhibited. The morphology and the size control by zeta-potential seem to be the result of thermodynamics rather than classical crystalline kinetics. The particle sizes were in the range of 0.4-0.6, 0.3-0.4 micrometer. After thermolysis, the spinel-type Co_3O_4 particles were produced. The morphologies of Co_3O_4 particles were similar to that of their precursors.