STUDY OF OUT-TIME ON THE PROCESSING AND PROPERTIES OF IM7/977-3 COMPOSITES

摘要

The capability to manufacture large structures leads to weight savings and reduced risk relative to joining smaller components. However, manufacture of increasingly large composite components is pushing the out-life limits of epoxy/ carbon fiber prepreg. IM7/977-3 is an autoclave processable prepreg material, commonly used in aerospace structures. The out-life limit is reported as 30 days by the manufacturer. The purpose of this work was to evaluate the material processability and composite properties of 977-3 resin and IM7/977-3 prepreg that had been aged at room temperature for up to 60 days. The neat resin was evaluated by differential scanning calorimetry, DSC, to characterize cure behavior of the aged material, as well as any change in activation energy. The rise in the modulus of the uncured prepreg was monitored throughout the 60 days by dynamic mechanical analysis, DMA. Composite panels made of the fresh and aged prepreg material were also characterized by DMA. The overall test results suggested that IM7/977-3 was a robust material that offered quality laminates throughout this aging process when processed by autoclave.