Martensitic transformation behavior under magnetic field in Co-Ni-Al ferromagnetic shape memory alloys

摘要

Effect of the magnetic field on the martensitic transformation of Co-Ni-Al single-crystal was investigated by differential thermal analysis (DTA) and the in-situ microstructure observation under magnetic field. The martensitic transformation temperatures M_s and M_f of the Co_(34.5)Ni_(35.5)Al_(30) (at.%) single-crystal specimen showing the martensitic transformation from the paramagnetic austenite (B2) to the ferromagnetic martensite (L1_0) slightly increased under the magnetic field and those temperatures shifts were about 1.3 ℃ at 1.0 T. It was also observed in the Co_(34.5)Ni_(35.5)Al_(30) single-crystal specimen that the phase boundaries between the austenite and the martensite slightly move by applying the magnetic field of 1.0 T. These results are discussed on the basis of a thermodynamic stability of the martensite phase under the magnetic field. The martensitic and the magnetic transformation behaviors of the Ni-Al-Co alloys are also reviewed.