The preparation of high concentration silver nanoplates with liquid-phase reduction method

摘要

Silver nanoplates,also referred to as nanoprisms or nanodisks,are two-dimensional plasmonic nanostructures that have attracted intensive attention due to their strong shape-dependent optical properties and related applications.In order to obtain the silver nanoplates with high concentration,the liquid-phase reduction method was adopted.Silver nanoparticles colloid was obtained by reducing the high molar concentration of AgNO3 (up to 3.17 M) with the hydrazine hydrate (H4N2 ? H2O) as reductant in the presence of polyethylene pyrrole (PVP) as the protectant.0.5 M Sodium Citrate is introduced into the precursor aqueous which containing AgNO3 and PVP,the molar ratio of PVP to AgNO3 was tuned from 0.64 to 1.5.When molar is 1.5,the mainly particles are silver nanospheres,on the contrary,the nanospheres are transferred into nanoplates as the ratio decreased gradually,until the mainly product are nanoplates.The constituent of the silver nano-clusters was established by performing the Powder X-ray diffraction.The nano-silver dispersion with average diameter is about 113.2 nm were finally deserved.The size distribution of the silver nanoparticles is recorded by the Zeta potential analyzer.Scanning electron microscope (SEM) was used to characterize the morphology of the nano-silver particles.The silver content is about 3％.Nano-silver colloid is obtained and purified by centrifugation and wash with deionized water and ethanol.Then,water-based silver conductive ink is obtained by adding some amount deionized water and additives and adjusted parameters,which could be widely used in printed electronics.